ASTM A276 Grade 444 Annealed; Hot-Finished
Equivalent material: DIN 1.4521, DIN X2CrMoTi18-2, AFNOR Z3CDT18-02, BS X2CrMoTi18-2, AISI 444, SAE 444, JIS SUS444, JIS SUS444TP, JIS SUS444TB, EN X2CrMoTi18-2, EN 1.4521, GB 019Cr19Mo2NbTi, ASTM S44400, UNS S44400, ASTM 18Cr-2Mo, ASTM 18-2
ASTM A276 Grade 444 Annealed; Hot-Finished general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.6 - 7.8 g/cm³ |
Typical for Ferritic Stainless Steel |
ASTM A276 Grade 444 Annealed; Hot-Finished thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 9.3E-6 - 1.2E-5 1/K |
Typical for Ferritic Stainless Steel |
| Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 420 - 586 J/(kg·K) |
Typical for Ferritic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 22 W/(m·K) |
Typical for Ferritic Stainless Steel |
ASTM A276 Grade 444 Annealed; Hot-Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0.025 % |
| Chromium |
Chromium of 17.5 - 19.5 % |
| Manganese |
Manganese of 1 % |
| Molybdenum |
Molybdenum of 1.75 - 2.5 % |
| Nickel |
Nickel of 1 % |
| Nitrogen |
Nitrogen of 0.04 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A276 Grade 444 Annealed; Hot-Finished electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
ASTM A276 Grade 444 Annealed; Hot-Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 220 GPa |
Typical for Ferritic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 217 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 415 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 310 MPa |
- |