ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished
Equivalent material: AMS 5615, ASTM MT414, UNS S41400
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished chemical
| Property |
Value |
| Carbon |
Carbon of 0.15 % |
| Chromium |
Chromium of 11.5 - 13.5 % |
| Manganese |
Manganese of 1 % |
| Nickel |
Nickel of 1.25 - 2.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.03 % |
ASTM A276 Grade 414 Hardened and tempered at a relatively high temperature; Hot-Finished or Cold-Finished mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 15 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 45 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 620 MPa |
- |