ASTM A234 Grade WPR Heat-Treated
Equivalent material: UNS K22035
ASTM A234 Grade WPR Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 8.8 g/cm³ | Typical for Nickel Steel |
ASTM A234 Grade WPR Heat-Treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Melting point | - | Melting point of 1316 - 1595 °C | Typical for Nickel Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 456 J/(kg·K) | Typical for Nickel Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 10 - 50 W/(m·K) | Typical for Nickel Steel |
ASTM A234 Grade WPR Heat-Treated chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.2 % |
| Copper | Copper of 0.75 - 1.25 % |
| Manganese | Manganese of 0.4 - 1.06 % |
| Nickel | Nickel of 1.6 - 2.24 % |
| Phosphorus | Phosphorus of 0.05 % |
| Sulfur | Sulfur of 0.05 % |
ASTM A234 Grade WPR Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Nickel Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 20 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Nickel Steel |
| Shear modulus | 23.0 °C | Shear modulus of 76 GPa | Typical for Nickel Steel |
| Tensile strength | 23.0 °C | Tensile strength of 435 - 605 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 315 MPa | - |