ASTM A234 Grade WP1 Heat-Treated
ASTM A234 Grade WP1 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.8 - 7.9 g/cm³ | Typical for Molybdenum Steel |
ASTM A234 Grade WP1 Heat-Treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.29E-5 1/K | Typical for Molybdenum Steel |
| Melting point | - | Melting point of 1382 - 1529 °C | Typical for Molybdenum Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 456 J/(kg·K) | Typical for Molybdenum Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 37 - 48 W/(m·K) | Typical for Molybdenum Steel |
ASTM A234 Grade WP1 Heat-Treated chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.28 % |
| Manganese | Manganese of 0.3 - 0.9 % |
| Molybdenum | Molybdenum of 0.44 - 0.65 % |
| Phosphorus | Phosphorus of 0.05 % |
| Silicon | Silicon of 0.1 - 0.5 % |
| Sulfur | Sulfur of 0.045 % |
ASTM A234 Grade WP1 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Molybdenum Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 14 - 22 % | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Molybdenum Steel |
| Tensile strength | 23.0 °C | Tensile strength of 380 - 550 MPa | - |
| Yield strength Rp0.2 | 23.0 °C | Yield strength Rp0.2 of 205 MPa | - |