ASTM A231 Grade 6150 Annealed and Cold-Drawn or Oil-Tempered
Equivalent material: AISI 6150, AISI 6150H, SAE 6150, SAE 6150H, ASTM A752 Grade 6150, ASTM A304 Grade 6150H, ASTM A322 Grade 6150
ASTM A231 Grade 6150 Annealed and Cold-Drawn or Oil-Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Chromium Vanadium Steel |
ASTM A231 Grade 6150 Annealed and Cold-Drawn or Oil-Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
Typical for Chromium Vanadium Steel |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Vanadium Steel |
ASTM A231 Grade 6150 Annealed and Cold-Drawn or Oil-Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.48 - 0.53 % |
| Chromium |
Chromium of 0.8 - 1.1 % |
| Manganese |
Manganese of 0.7 - 0.9 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0.04 % |
| Vanadium |
Vanadium of 0.15 % |
ASTM A231 Grade 6150 Annealed and Cold-Drawn or Oil-Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Chromium Vanadium Steel |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Vanadium Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 40 - 45 % |
- |
| Tensile strength |
23.0 °C |
Tensile strength of 1320 - 2260 MPa |
- |
Be at the forefront of industry advancements by incorporating our cutting-edge steel solutions.
-- Our promise