ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered
Equivalent material: ASTM Grade WCC
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered general
| Property |
Temperature |
Value |
Comment |
| Density |
20.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
20.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered chemical
| Property |
Value |
| Carbon |
Carbon of 0.25 % |
| Chromium |
Chromium of 0.5 % |
| Copper |
Copper of 0.3 % |
| Manganese |
Manganese of 1.2 % |
| Molybdenum |
Molybdenum of 0.2 % |
| Nickel |
Nickel of 0.5 % |
| Phosphorus |
Phosphorus of 0.04 % |
| Silicon |
Silicon of 0.6 % |
| Sulfur |
Sulfur of 0.035 % |
| Vanadium |
Vanadium of 0.03 % |
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered magnetic
| Property |
Temperature |
Value |
Comment |
| Curie temperature |
20.0 °C |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
20.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A216 Grade WCC Annealed, or Normalized, or Normalized and Tempered mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
20.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
20.0 °C |
Elongation A50 of 22 % |
- |
| Poisson's ratio |
20.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Reduction of area |
20.0 °C |
Reduction of area of 35 % |
- |
| Shear modulus |
20.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
20.0 °C |
Tensile strength of 485 - 655 MPa |
- |
| Yield Strength Rp0.2, short transverse |
20.0 °C |
Yield Strength Rp0.2, short transverse of 275 MPa |
- |