ASTM A213 Grade T911 Heat-Treated
Equivalent material: UNS K91061
ASTM A213 Grade T911 Heat-Treated general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
Typical for Steel |
ASTM A213 Grade T911 Heat-Treated chemical
| Property |
Value |
| Aluminium |
Aluminium of 0.02 % |
| Boron |
Boron of 3E-4 - 6E-3 % |
| Carbon |
Carbon of 0.09 - 0.13 % |
| Chromium |
Chromium of 8.5 - 9.5 % |
| Manganese |
Manganese of 0.3 - 0.6 % |
| Molybdenum |
Molybdenum of 0.9 - 1.1 % |
| Nickel |
Nickel of 0.4 % |
| Niobium |
Niobium of 0.06 - 0.1 % |
| Nitrogen |
Nitrogen of 0.04 - 0.09 % |
| Phosphorus |
Phosphorus of 0.02 % |
| Silicon |
Silicon of 0.1 - 0.5 % |
| Sulfur |
Sulfur of 0.01 % |
| Tungsten |
Tungsten of 0.9 - 1.1 % |
| Vanadium |
Vanadium of 0.18 - 0.25 % |
ASTM A213 Grade T911 Heat-Treated mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 190 - 210 GPa |
Typical for Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 20 % |
- |
| Hardness, Brinell |
23.0 °C |
Hardness, Brinell of 250 [-] |
- |
| Hardness, Rockwell C |
23.0 °C |
Hardness, Rockwell C of 25 [-] |
- |
| Hardness, Vickers |
23.0 °C |
Hardness, Vickers of 265 [-] |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 620 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |