ASTM A213 Grade S32050 Heat-Treated
Equivalent material: UNS S32050
ASTM A213 Grade S32050 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 8.8 g/cm³ | Typical for Nickel Steel |
ASTM A213 Grade S32050 Heat-Treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Melting point | - | Melting point of 1316 - 1595 °C | Typical for Nickel Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 456 J/(kg·K) | Typical for Nickel Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 10 - 50 W/(m·K) | Typical for Nickel Steel |
ASTM A213 Grade S32050 Heat-Treated chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.03 % |
| Chromium | Chromium of 22 - 24 % |
| Manganese | Manganese of 1.5 % |
| Molybdenum | Molybdenum of 6 - 6.8 % |
| Nickel | Nickel of 20 - 23 % |
| Nitrogen | Nitrogen of 0.21 - 0.32 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 1 % |
| Sulfur | Sulfur of 0.02 % |
ASTM A213 Grade S32050 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 200 - 215 GPa | Typical for Nickel Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 40 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 256 [-] | - |
| Hardness, Rockwell B | 23.0 °C | Hardness, Rockwell B of 100 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.29 [-] | Typical for Nickel Steel |
| Shear modulus | 23.0 °C | Shear modulus of 76 GPa | Typical for Nickel Steel |
| Tensile strength | 23.0 °C | Tensile strength of 675 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 330 MPa | - |