ASTM A213 Grade S30432 Heat-Treated
Equivalent material: DIN 1.4907, EN X10CrNiCuNb18-9-3, EN 1.4907, UNS S30432
ASTM A213 Grade S30432 Heat-Treated general
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Density | 23.0 °C | Density of 7.9 - 8.2 g/cm³ | Typical for Austenitic Stainless Steel |
ASTM A213 Grade S30432 Heat-Treated thermal
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Coefficient of thermal expansion | 23.0 °C | Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K | Typical for Austenitic Stainless Steel |
| Melting point | - | Melting point of 1230 - 1480 °C | Typical for Austenitic Stainless Steel |
| Specific heat capacity | 23.0 °C | Specific heat capacity of 440 J/(kg·K) | Typical for Austenitic Stainless Steel |
| Thermal conductivity | 23.0 °C | Thermal conductivity of 11 - 21 W/(m·K) | Typical for Austenitic Stainless Steel |
ASTM A213 Grade S30432 Heat-Treated chemical
| Property | Value |
|---|---|
| Carbon | Carbon of 0.07 - 0.13 % |
| Chromium | Chromium of 17 - 19 % |
| Manganese | Manganese of 1 % |
| Nickel | Nickel of 7.5 - 10.5 % |
| Niobium | Niobium of 0.3 - 0.6 % |
| Nitrogen | Nitrogen of 0.05 - 0.12 % |
| Phosphorus | Phosphorus of 0.04 % |
| Silicon | Silicon of 0.3 % |
| Sulfur | Sulfur of 0.01 % |
ASTM A213 Grade S30432 Heat-Treated electrical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Electrical resistivity | 23.0 °C | Electrical resistivity of 8.5E-7 Ω·m | Typical for Austenitic Stainless Steel |
ASTM A213 Grade S30432 Heat-Treated mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
| Elastic modulus | 23.0 °C | Elastic modulus of 195 GPa | Typical for Austenitic Stainless Steel |
| Elongation A50 | 23.0 °C | Elongation A50 of 35 % | - |
| Hardness, Brinell | 23.0 °C | Hardness, Brinell of 219 [-] | - |
| Hardness, Rockwell B | 23.0 °C | Hardness, Rockwell B of 95 [-] | - |
| Hardness, Vickers | 23.0 °C | Hardness, Vickers of 230 [-] | - |
| Poisson's ratio | 23.0 °C | Poisson's ratio of 0.3 [-] | Typical for Austenitic Stainless Steel |
| Shear modulus | 23.0 °C | Shear modulus of 77 GPa | Typical for Austenitic Stainless Steel |
| Tensile strength | 23.0 °C | Tensile strength of 590 MPa | - |
| Yield strength | 23.0 °C | Yield strength of 235 MPa | - |