ASTM A182 Grade F44 Solution-Annealed
Equivalent material: DIN 1.4547, DIN X1CrNiMoCuN20-18-7, AFNOR Z1CNDU20-18-06Az, BS X1CrNiMoCuN20-18-7, AISI F44, AISI 254SMO, SAE F44, SAE 254SMO, JIS SUS312L, JIS SUS 312LTB, EN X1CrNiMoCuN20-18-7, EN 1.4547, ISO X1CrNiMoCuN20-18-7, ISO 4547-312-54-I, ISO AM45A, ISO 34, ASTM Grade F44, ASTM Grade 8MLCuNA, UNS S31254
ASTM A182 Grade F44 Solution-Annealed general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.9 - 8.2 g/cm³ |
Typical for Austenitic Stainless Steel |
ASTM A182 Grade F44 Solution-Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.7E-5 - 1.9E-5 1/K |
Typical for Austenitic Stainless Steel |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 440 J/(kg·K) |
Typical for Austenitic Stainless Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 11 - 21 W/(m·K) |
Typical for Austenitic Stainless Steel |
ASTM A182 Grade F44 Solution-Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.07 % |
| Chromium |
Chromium of 19 - 21 % |
| Manganese |
Manganese of 2 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 32 - 38 % |
| Niobium |
Niobium of 1 % |
| Phosphorus |
Phosphorus of 0.05 % |
| Silicon |
Silicon of 1 % |
| Sulfur |
Sulfur of 0.035 % |
ASTM A182 Grade F44 Solution-Annealed electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
ASTM A182 Grade F44 Solution-Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 195 GPa |
Typical for Austenitic Stainless Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 35 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Reduction of area |
23.0 °C |
Reduction of area of 50 % |
- |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 650 MPa |
- |
| Yield strength Rp0.2 |
23.0 °C |
Yield strength Rp0.2 of 300 MPa |
- |