ASTM A1008 BHS Grade 180 Bake-Hardenable
Equivalent material: DIN 1.0354, DIN H180BD, EN HX180BD, EN H180BD, EN 1.0354
ASTM A1008 BHS Grade 180 Bake-Hardenable general
| Property |
Temperature |
Value |
Comment |
| Density |
23.0 °C |
Density of 7.8 - 7.9 g/cm³ |
Typical for Low Carbon Steel |
ASTM A1008 BHS Grade 180 Bake-Hardenable thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.32E-5 - 1.38E-5 1/K |
Typical for Low Carbon Steel |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1480 - 1526 °C |
Typical for Low Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 465 J/(kg·K) |
Typical for Low Carbon Steel |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 25 - 93 W/(m·K) |
Typical for Low Carbon Steel |
ASTM A1008 BHS Grade 180 Bake-Hardenable chemical
| Property |
Value |
| Carbon |
Carbon of 0.12 % |
| Chromium |
Chromium of 0.15 % |
| Copper |
Copper of 0.2 % |
| Manganese |
Manganese of 1.5 % |
| Molybdenum |
Molybdenum of 0.06 % |
| Nickel |
Nickel of 0.2 % |
| Niobium |
Niobium of 8E-3 % |
| Phosphorus |
Phosphorus of 0.12 % |
| Sulfur |
Sulfur of 0.03 % |
| Titanium |
Titanium of 8E-3 % |
| Vanadium |
Vanadium of 8E-3 % |
ASTM A1008 BHS Grade 180 Bake-Hardenable magnetic
| Property |
Value |
Comment |
| Curie temperature |
Curie temperature of 770 °C |
Typical for Low Carbon Steel |
ASTM A1008 BHS Grade 180 Bake-Hardenable electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
ASTM A1008 BHS Grade 180 Bake-Hardenable mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 - 215 GPa |
Typical for Low Carbon Steel |
| Elongation A50 |
23.0 °C |
Elongation A50 of 30 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Low Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 82 GPa |
Typical for Low Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 300 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 180 MPa |
- |
Count on us as your trusted partner for all your steel needs, from sourcing to delivery.
-- Our promise
Similar or equivalent steel materials
- ASTM A653 BHS Grade 180
- EN 10292 Grade HX180BD +Z, +ZF, +ZA, +AZ, +AS,hot rolled or cold rolled, hot dip coated
- EN 10292 Grade HX180BD hot rolled or cold rolled, hot dip coated,+Z, +ZF, +ZA, +AZ, +AS
- DIN 5512-2 Grade St14Cu3