AISI 6150 Annealed
Equivalent material: DIN 1.8159, DIN GS-50CrV4, DIN 50CrV4, DIN G51CrV4, DIN 51CrV4, AFNOR 50CrV4, BS 735A50, BS 50CrV4, UNI 50CrV4, SS 2230, AISI 6150H, SAE 6150, SAE 6150H, JIS SUP10, JIS SUP10M, EN 50CrV4, EN 51CrV4, EN 1.8159, GOST 50HFA, GOST 50HGFA, GB 50CrV4, ASTM A752 Grade 6150, ASTM A304 Grade 6150H, ASTM A231 Grade 6150, ASTM A322 Grade 6150
AISI 6150 Annealed general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 6150 Annealed thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Melting point |
- |
Melting point of 1382 - 1529 °C |
Typical for Chromium Vanadium Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
AISI 6150 Annealed chemical
| Property |
Value |
| Carbon |
Carbon of 0.48 - 0.53 % |
| Chromium |
Chromium of 0.8 - 1.1 % |
| Iron |
Iron of 96.7 - 97.7 % |
| Manganese |
Manganese of 0.7 - 0.9 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0.15 - 0.35 % |
| Sulfur |
Sulfur of 0 - 0.04 % |
| Vanadium |
Vanadium of 0.15 - 0.3 % |
AISI 6150 Annealed mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 23 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Chromium Vanadium Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 670 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 420 MPa |
- |