AISI 440A Hardened
Equivalent material: DIN 1.4109, DIN X 65 CrMo 14, DIN X70CrMo15, SAE 440A, EN X70CrMo15, EN 1.4109, ISO S, ASTM MT440A, ASTM 440A, UNS S44002
AISI 440A Hardened general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.7 g/cm³ |
AISI 440A Hardened thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1E-5 1/K |
| Melting point |
- |
Melting point of 1370 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 460 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 30 W/(m·K) |
AISI 440A Hardened chemical
| Property |
Value |
| Carbon |
Carbon of 0.6 - 0.75 % |
| Chromium |
Chromium of 14 - 18 % |
| Iron |
Iron of 78.4 - 85 % |
| Manganese |
Manganese of 0 - 1 % |
| Molybdenum |
Molybdenum of 0 - 0.8 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.015 % |
AISI 440A Hardened electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 Ω·m |
Typical for Martensitic Stainless Steel |
AISI 440A Hardened mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 5 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Martensitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Martensitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1650 MPa |
- |