AISI 316L 1/8-Hard
Equivalent material: DIN 1.4404, DIN X2CrNiMo18-10, DIN X2CrNiMo17-12-2, DIN G-X2CrNiMoN18-14, DIN GX2CrNiMoN18-14, DIN X2CrNiMoN17-12-2, DIN X2CrNiMo17-13-2, DIN G-X2CrNiMoN18-10, AFNOR Z2CND17-12, BS 316S12, UNI X2CrNiMo1712, SS 2343, SS 2348, SS 2553, SAE 316L, JIS SUS316L, JIS SCS16, EN X2CrNiMo17-12-2, EN 1.4404, GOST 03Ch17N13M2, GB 022Cr17Ni12Mo2, ASTM 316L, UNS S31603, IS X02Cr17Ni12Mo2, DIN 1.4409, BS 316C12, JIS SCS16A, EN GX2CrNiMo19-11-2, EN 1.4409, ASTM CF3M, ASTM CF3MA, UNS J92800, DIN 1.4432, AFNOR Z3CND17-12-03, BS 316S13, JIS SUS316LFB, JIS SUSF316L, EN X2CrNiMo17-12-3, EN 1.4432, GOST 06Ch17N13M3-WD, DIN 1.4435, DIN X2CrNiMo18-14-3, AFNOR Z3CND18-14-03, BS 316S11, BS 316S31, SS 2353, UNE X2CrNiMo18-14-3, AISI 316LMo, SAE 316LMo, JIS SUS316LTBS, JIS SUS316LTP, JIS SUS316LTPY, JIS SUS316LTB, JIS SUSY316L, JIS SUS316J1L, JIS SUSY316J1L, EN X2CrNiMo18-14-3, EN 1.4435, GOST 03Ch17N14M3, GB 00Cr18Ni15Mo3
AISI 316L 1/8-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.9 g/cm³ |
AISI 316L 1/8-Hard thermal
| Property |
Temperature |
Value |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.6E-5 1/K |
| Melting point |
- |
Melting point of 1380 °C |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 490 J/(kg·K) |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
AISI 316L 1/8-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.03 % |
| Chromium |
Chromium of 16 - 19 % |
| Iron |
Iron of 59.8 - 72 % |
| Manganese |
Manganese of 0 - 2 % |
| Molybdenum |
Molybdenum of 2 - 3 % |
| Nickel |
Nickel of 10 - 15 % |
| Nitrogen |
Nitrogen of 0 - 0.1 % |
| Phosphorus |
Phosphorus of 0 - 0.05 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 316L 1/8-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 316L 1/8-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 29 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 790 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 440 MPa |
- |