AISI 304N Annealed
Equivalent material: DIN 1.4315, BS 304S65, SAE 304N, JIS SUS304N1, JIS SCS13A, JIS SUSF304N, EN X5CrNiN19-9, EN 1.4315, ASTM TP304N, UNS S30451, ASTM 304N, ASTM S30451, JIS SUSF304N, ASTM F304N, ASTM Grade 8N, ASTM 304N, ASTM FP304N, ASTM Grade B8N, ASTM Grade B8NA, ASTM Grade 8NA
AISI 304N Annealed general
Property |
Temperature |
Value |
Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 304N Annealed thermal
Property |
Temperature |
Value |
Comment |
Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
Melting point |
- |
Melting point of 1425 - 1530 °C |
Typical for Ferritic Stainless Steel |
Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
AISI 304N Annealed chemical
Property |
Value |
Carbon |
Carbon of 0 - 0.08 % |
Chromium |
Chromium of 18 - 20 % |
Iron |
Iron of 65.7 - 73.9 % |
Manganese |
Manganese of 0 - 2 % |
Nickel |
Nickel of 8 - 11 % |
Nitrogen |
Nitrogen of 0.1 - 0.22 % |
Phosphorus |
Phosphorus of 0 - 0.05 % |
Silicon |
Silicon of 0 - 1 % |
Sulfur |
Sulfur of 0 - 0.03 % |
AISI 304N Annealed electrical
Property |
Temperature |
Value |
Comment |
Electrical resistivity |
23.0 °C |
Electrical resistivity of 6E-7 - 7.5E-7 Ω·m |
Typical for Ferritic Stainless Steel |
AISI 304N Annealed mechanical
Property |
Temperature |
Value |
Comment |
Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
Elongation |
23.0 °C |
Elongation of 35 % |
- |
Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Ferritic Stainless Steel |
Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Ferritic Stainless Steel |
Tensile strength |
23.0 °C |
Tensile strength of 630 MPa |
- |
Yield strength |
23.0 °C |
Yield strength of 280 MPa |
- |