AISI 201 Full-Hard
Equivalent material: DIN 1.4372, DIN X12CrMnNiN17-7-5, SAE 201, JIS SUS201, EN X12CrMnNiN17-7-5, EN 1.4372, ISO X12CrMnNiN17-7-5, ISO 4372-201-00-I, ISO AP29O, ISO 13, ASTM TP201, ASTM 201-1, ASTM 201-2, UNS S20100, ASTM 201
AISI 201 Full-Hard general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.7 g/cm³ |
AISI 201 Full-Hard thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.3E-5 1/K |
- |
| Melting point |
- |
Melting point of 1230 - 1480 °C |
Typical for Austenitic Stainless Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 500 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 15 W/(m·K) |
- |
AISI 201 Full-Hard chemical
| Property |
Value |
| Carbon |
Carbon of 0 - 0.15 % |
| Chromium |
Chromium of 16 - 18 % |
| Iron |
Iron of 67.5 - 75 % |
| Manganese |
Manganese of 5.5 - 7.5 % |
| Nickel |
Nickel of 3.5 - 5.5 % |
| Nitrogen |
Nitrogen of 0 - 0.25 % |
| Phosphorus |
Phosphorus of 0 - 0.06 % |
| Silicon |
Silicon of 0 - 1 % |
| Sulfur |
Sulfur of 0 - 0.03 % |
AISI 201 Full-Hard electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 8.5E-7 Ω·m |
Typical for Austenitic Stainless Steel |
AISI 201 Full-Hard mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 200 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 4.6 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.3 [-] |
Typical for Austenitic Stainless Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 77 GPa |
Typical for Austenitic Stainless Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 1470 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 1110 MPa |
- |