AISI 1541 Annealed And Cold Drawn
Equivalent material: DIN 1.1127, DIN 38Mn6, AFNOR 38Mn6, BS 38Mn6, SAE 1541, JIS SMn438, JIS SMn438H, JIS SMn438M, EN 38Mn6, EN 1.1127, GOST 40G2, GB/T 40Mn2, GB/T A00402, ASTM 1541, ASTM Grade 1541, UNS G15410, IS SMn438, DIN 1.1167, DIN 36Mn5, AFNOR 40M5, BS 150M36, BS 120M36, AISI 1335H, AISI 1335, SAE 1335H, SAE 1335, EN 1.1167, GOST 35GL, GOST 35G2, GB 35Mn2, GB A00352, ASTM 1335, UNS H13350, UNS G13350
AISI 1541 Annealed And Cold Drawn general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1541 Annealed And Cold Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1380 - 1514 °C |
Typical for Medium Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 21 - 52 W/(m·K) |
Typical for Medium Carbon Steel |
AISI 1541 Annealed And Cold Drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.36 - 0.44 % |
| Iron |
Iron of 97.8 - 98.3 % |
| Manganese |
Manganese of 1.4 - 1.7 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1541 Annealed And Cold Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1541 Annealed And Cold Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for Medium Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 75 - 80 GPa |
Typical for Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 750 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 630 MPa |
- |