AISI 1086 Spheroidized And Cold Drawn
Equivalent material: DIN 1.1269, DIN Ck85, DIN C85S, AFNOR C85S, AFNOR XC90, AFNOR C90RR, BS C85S, BS CS80, BS 80HS, BS 80CS, SAE 1086, JIS SK85-CSP, JIS SWRH82A, EN C85S, EN 1.1269, ISO C85S, GOST 85, GOST 85A, GB/T 85, GB/T U20852, UNS G10860, DIN 1.0616, DIN D 85-2, DIN C86D, AFNOR C86D, BS C86D, AISI 1080, SAE 1080, JIS CS85, EN C86D, EN 1.0616, ISO C86D, ISO CS85, GB 85, GB U53862, GB U20852, GB/T C86D, GB/T U53862, GB/T U59863, ASTM 1080, UNS G10800
AISI 1086 Spheroidized And Cold Drawn general
| Property |
Temperature |
Value |
| Density |
23.0 °C |
Density of 7.8 g/cm³ |
AISI 1086 Spheroidized And Cold Drawn thermal
| Property |
Temperature |
Value |
Comment |
| Coefficient of thermal expansion |
23.0 °C |
Coefficient of thermal expansion of 1.2E-5 1/K |
- |
| Max service temperature |
- |
Max service temperature of 500 °C |
Typical for Carbon Steel |
| Melting point |
- |
Melting point of 1289 - 1478 °C |
Typical for High Carbon Steel |
| Specific heat capacity |
23.0 °C |
Specific heat capacity of 450 J/(kg·K) |
- |
| Thermal conductivity |
23.0 °C |
Thermal conductivity of 36 W/(m·K) |
Typical for High Carbon Steel |
AISI 1086 Spheroidized And Cold Drawn chemical
| Property |
Value |
| Carbon |
Carbon of 0.8 - 0.93 % |
| Iron |
Iron of 98.5 - 98.9 % |
| Manganese |
Manganese of 0.3 - 0.5 % |
| Phosphorus |
Phosphorus of 0 - 0.04 % |
| Sulfur |
Sulfur of 0 - 0.05 % |
AISI 1086 Spheroidized And Cold Drawn electrical
| Property |
Temperature |
Value |
Comment |
| Electrical resistivity |
23.0 °C |
Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m |
Typical for Carbon Steel |
AISI 1086 Spheroidized And Cold Drawn mechanical
| Property |
Temperature |
Value |
Comment |
| Elastic modulus |
23.0 °C |
Elastic modulus of 210 GPa |
- |
| Elongation |
23.0 °C |
Elongation of 12 % |
- |
| Poisson's ratio |
23.0 °C |
Poisson's ratio of 0.29 [-] |
Typical for High Carbon Steel |
| Shear modulus |
23.0 °C |
Shear modulus of 81 GPa |
Typical for High Carbon Steel |
| Tensile strength |
23.0 °C |
Tensile strength of 770 MPa |
- |
| Yield strength |
23.0 °C |
Yield strength of 590 MPa |
- |