AISI 1084 Hot Rolled

AISI 1084 Hot Rolled

Equivalent material: DIN 1.0628, DIN D 88-2, DIN C88D, AFNOR C88D, BS C88D, SAE 1084, JIS SWRS87, EN C88D, EN 1.0628, ISO C88D, GB U53787, GB YL87, GB C88D, GB/T C88D, GB/T U53882, GB/T U53877, GB/T YL87, GB/T U59883, UNS G10840, DIN 1.1272, DIN D88-3, DIN C88D2, AFNOR C88D2, BS C88D2, EN C98D2, EN 1.1272, ISO C88D2, GB/T C88D2

AISI 1084 Hot Rolled general

Property Temperature Value
Density 23.0 °C Density of 7.8 g/cm³

AISI 1084 Hot Rolled thermal

Property Temperature Value Comment
Coefficient of thermal expansion 23.0 °C Coefficient of thermal expansion of 1.2E-5 1/K -
Max service temperature - Max service temperature of 500 °C Typical for Carbon Steel
Melting point - Melting point of 1289 - 1478 °C Typical for High Carbon Steel
Specific heat capacity 23.0 °C Specific heat capacity of 450 J/(kg·K) -
Thermal conductivity 23.0 °C Thermal conductivity of 36 W/(m·K) Typical for High Carbon Steel

AISI 1084 Hot Rolled chemical

Property Value
Carbon Carbon of 0.8 - 0.93 %
Iron Iron of 98.1 - 98.6 %
Manganese Manganese of 0.6 - 0.9 %
Phosphorus Phosphorus of 0 - 0.04 %
Sulfur Sulfur of 0 - 0.05 %

AISI 1084 Hot Rolled electrical

Property Temperature Value Comment
Electrical resistivity 23.0 °C Electrical resistivity of 1.43E-7 - 1.74E-7 Ω·m Typical for Carbon Steel

AISI 1084 Hot Rolled mechanical

Property Temperature Value Comment
Elastic modulus 23.0 °C Elastic modulus of 210 GPa -
Elongation 23.0 °C Elongation of 12 % -
Poisson's ratio 23.0 °C Poisson's ratio of 0.29 [-] Typical for High Carbon Steel
Shear modulus 23.0 °C Shear modulus of 81 GPa Typical for High Carbon Steel
Tensile strength 23.0 °C Tensile strength of 940 MPa -
Yield strength 23.0 °C Yield strength of 520 MPa -